产品别名 |
NILAMID,30GF增强PA66热稳定 |
面向地区 |
30%GF增强PA66 NILAMID A3 HH GF30热稳定
Density (23°C) | 1.37 | g/cm³ | ISO 1183 |
Molding Shrinkage | ISO 294-4 | ||
Across Flow : 23°C | 0.75 | % | |
Flow : 23°C | 0.40 | % | |
Water Absorption | ISO 62 | ||
24 hr, 23°C | 1.0 | % | |
Saturation, 23°C | 5.5 | % |
Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus (23°C) | 9800 | MPa | ISO 527-2 |
Tensile Stress (Yield, 23°C) | 185 | MPa | ISO 527-2 |
Tensile Strain (Break, 23°C) | 2.5 | % | ISO 527-2 |
Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength | ISO 179/1eA | ||
-30°C | 9.5 | kJ/m² | |
23°C | 12 | kJ/m² | |
Charpy Unnotched Impact Strength | ISO 179/1eU | ||
-30°C | 41 | kJ/m² | |
23°C | 53 | kJ/m² | |
Notched Izod Impact Strength | ISO 180/A | ||
-30°C | 8.0 | kJ/m² | |
23°C | 10 | kJ/m² |
Thermal | Nominal Value | Unit | Test Method |
Heat Deflection Temperature | |||
0.45 MPa, Unannealed | 260 | °C | ISO 75-2/B |
1.8 MPa, Unannealed | 250 | °C | ISO 75-2/A |
Continuous Use Temperature 3 | 140 | °C | IEC 60216 |
Ball Pressure Test | IEC 60695-10-2 | ||
125°C | Pass | ||
165°C | Pass |
Electrical | Nominal Value | Unit | Test Method |
Surface Resistivity 4 | 1.0E+13 | ohms | IEC 60093 |
Volume Resistivity (23°C) | 1.0E+15 | ohms·cm | IEC 60093 |
Electric Strength (2.00 mm) | 21 | kV/mm | IEC 60243-1 |
Comparative Tracking Index (3.20 mm, Solution A) | 500 | V | IEC 60112 |
PA66美国杜邦70G13L 70G13HS1L玻纤增强13%高强度 。
PA66美国杜邦70G33L 70G33HS1L高强度 玻纤增强33% 。
PA66塑胶原料美国杜邦70G43L 高强度43%玻纤增强。
PA66美国杜邦80G33HS1-L抗冲击性 玻纤增强33% 强度 。
PA66塑胶原料美国杜邦FR10 FR15 FR50 FR60玻纤增强无卤阻燃级UL94 V-0等级
PA66美国杜邦ST801特殊级 韧性 的耐冲击性。
PA66塑胶原料日本东丽CM3001G-30一般用途 玻纤增强30%。
PA66日本东丽CM3001-N CM3006标准级尼龙-66未强化。
PA66日本东丽CM3004G-30玻纤增强30%含卤阻燃级。
PA66日本东丽CM3004-V0尼龙66未强化,无卤阻燃级。
PA66塑胶原料日本旭化成1300G高强度 高刚性 玻纤增强33%。
PA66日本旭化成1300S平衡的流动性和机械性能。
PA66日本旭化成1402S具有良好的抗热老化性能。
PA66日本旭化成FR200 FR370阻燃级UL94 V-0;不含卤素和磷。
30%GF增强PA66 NILAMID A3 HH GF30热稳定