产品别名 |
NILAMID,耐老化耐水解PA66 |
面向地区 |
批发35%玻纤PA66 NILAMID A3 HHR GF35耐老化耐水解
| ISO | dry / cond | Unit | Test Standard |
| Density | 1410 / - | kg/m³ | ISO 1183 |
| Molding shrinkage, parallel | 0.3 | % | ISO 294-4, 2577 |
| Molding shrinkage, normal | 0.5 | % | ISO 294-4, 2577 |
| Water absorption, 23°C-sat | 4.5 / * | % | ISO 62 |
| Humidity absorption, 23°C/50%RH | 0.65 / * | % | ISO 62 |
| Tensile modulus | 11200 / - | MPa | ISO 527-2/1A |
| Tensile stress at break, 5mm/min | 175 / - | MPa | ISO 527-2/1A |
| Tensile strain at break, 5mm/min | 2.2 / - | % | ISO 527-2/1A |
| Flexural modulus, 23°C | 10000 / - | MPa | ISO 178 |
| Flexural stress at max. force | 270 / - | MPa | ISO 178 |
| Charpy impact strength, 23°C | 60 / - | kJ/m² | ISO 179/1eU |
| Charpy notched impact strength, 23°C | 12 / - | kJ/m² | ISO 179/1eA |
| Izod impact notched, 23°C | 10 / - | kJ/m² | ISO 180/1A |
| DTUL at 1.8 MPa | 251 / * | °C | ISO 75-1, -2 |
| DTUL at 0.45 MPa | 260 / * | °C | ISO 75-1, -2 |
| Flammability @0.8mm nom. thickn. | HB / * | class | UL 94 |
| Flammability @3.2mm nom. thickn. | HB / * | class | UL 94 |
| Other | dry / cond | Unit | Test Standard |
| Continuous service temperature | 130 / * | °C | DIN/IEC 60216-1 |
PA66半透明或不透明乳白色结晶形聚合物，广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等
PA66 聚酰胺66或尼龙66化学和物理特性PA66在聚酰胺材料中有较高的熔点。它是一种半晶体-晶体材料。PA66在较高温度也能保持较强的强度和刚度。在产品设计时，一定要考虑吸湿性对几何稳定性的影响。为了提高PA66的机械特性，经常加入各种各样的改性剂。玻璃就是常见的添加剂，有时为了提高抗冲击性还加入合成橡胶，如EPDM和SBR等。 PA66的粘性较低，因此流动性很好（但不如PA6）。
批发35%玻纤PA66 NILAMID A3 HHR GF35耐老化耐水解