产品别名 |
30玻纤增强高抗冲PA66,NILAMID |
面向地区 |
厂家高抗冲PA66 NILAMID A3 J GF30玻纤增强
| ISO | dry / cond | Unit | Test Standard |
| Density | 1300 / - | kg/m³ | ISO 1183 |
| Molding shrinkage, parallel | 0.4 - 0.8 | % | ISO 294-4, 2577 |
| Molding shrinkage, normal | 0.9 - 1.3 | % | ISO 294-4, 2577 |
| Water absorption, 23°C-sat | 6.5 / * | % | ISO 62 |
| Humidity absorption, 23°C/50%RH | 1.5 / * | % | ISO 62 |
| Tensile modulus | 7600 / - | MPa | ISO 527-2/1A |
| Tensile stress at break, 5mm/min | 150 / - | MPa | ISO 527-2/1A |
| Tensile strain at break, 5mm/min | 5.5 / - | % | ISO 527-2/1A |
| Charpy impact strength, 23°C | NB / - | kJ/m² | ISO 179/1eU |
| Charpy impact strength, -30°C | NB / - | kJ/m² | ISO 179/1eU |
| Charpy notched impact strength, 23°C | 21 / - | kJ/m² | ISO 179/1eA |
| Charpy notched impact strength, -30°C | 13 / - | kJ/m² | ISO 179/1eA |
| Ball indentation hardness, 30s | 150 | MPa | ISO 2039-1 |
| Melting point, peak | 260 | °C | ISO 3146 |
| DTUL at 1.8 MPa | 240 / * | °C | ISO 75-1, -2 |
| DTUL at 0.45 MPa | 250 / * | °C | ISO 75-1, -2 |
| Other | dry / cond | Unit | Test Standard |
| Continuous service temperature | 120 / * | °C | DIN/IEC 60216-1 |
PA66特性
1、具有优良的耐磨性、自润滑性，机械强度较高。但吸水性较大，因而尺寸稳定性较差
2、PA66在较高温度也能保持较强的强度和刚度。PA66在成型后仍然具有吸湿性，其程度主要取决于材料的组成、壁厚以及环境条件。
3、在产品设计时，一定要考虑吸湿性对几何稳定性的影响。为了提高PA66的机械特性，经常加入各种各样的改性剂。玻璃就是常见的添加剂，有时为了提高抗冲击性还加入合成橡胶，如EPDM和SBR等。PA66的粘性较低，因此流动性很好（但不如PA6）。这个性质可以用来加工很薄的元件。它的粘度对温度变化很敏感。
4、PA66的收缩率在1%~2%之间，加入玻璃纤维添加剂可以将收缩率降低到0.2%~1% 。收缩率在流程方向和与流程方向相垂直方向上的相异是较大的。PA66对许多溶剂具有抗溶性，但对酸和其它一些氯化剂的抵抗力较弱。
厂家高抗冲PA66 NILAMID A3 J GF30玻纤增强