产品别名

20玻纤PBT,激光焊接PBT

面向地区

经销朗盛20%玻纤PBT Pocan B3225LT激光焊接

PBT, 20 % glass fibers, injection molding, improved laser-transparency, NIR-laser transparent coloring (black)

Property		Test Condition	Unit	Standard	guide value
Rheological properties
C	Melt volume-flow rate	260 °C; 2.16 kg	cm³/(10 min)	ISO 1133-1	20
C	Molding shrinkage, parallel	60x60x2; 260 °C / MT 80 °C; 600 bar	%	ISO 294-4	0.5
C	Molding shrinkage, transverse	60x60x2; 260 °C / MT 80 °C; 600 bar	%	ISO 294-4	1.0
	Post- shrinkage, parallel	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.1
	Post- shrinkage, transverse	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.1
Mechanical properties (23 °C/50 % r. h.)
C	Tensile modulus	1 mm/min	MPa	ISO 527-1,-2	7100
C	Tensile Stress at break	5 mm/min	MPa	ISO 527-1,-2	120
C	Tensile Strain at break	5 mm/min	%	ISO 527-1,-2	3.2
	Izod impact strength	23 °C	kJ/m²	ISO 180-1U	35
	Flexural modulus	2 mm/min	MPa	ISO 178-A	7000
	Flexural strength	2 mm/min	MPa	ISO 178-A	195
	Flexural strain at flexural strength	2 mm/min	%	ISO 178-A	3.6
	Flexural stress at 3.5 % strain	2 mm/min	MPa	ISO 178-A	195
Thermal properties
C	Melting temperature	10 °C/min	°C	ISO 11357-1,-3	225
C	Temperature of deflection under load	1.80 MPa	°C	ISO 75-1,-2	205
C	Temperature of deflection under load	0.45 MPa	°C	ISO 75-1,-2	220
	Vicat softening temperature	50 N; 120 °C/h	°C	ISO 306	210