产品别名 |
激光焊接PA6耐热老化,德国朗盛PA6 |
面向地区 |
代理德国朗盛激光焊接PA6 Durethan BKV25H2.0LT耐热老化
Density (23°C) | 1.32 | -- | g/cm³ | ISO 1183 |
Apparent (Bulk) Density | 0.70 | -- | g/cm³ | ISO 60 |
Molding Shrinkage | ISO 2577 | |||
Across Flow : 120°C, 3.00 mm 3 | 0.14 | -- | % | |
Across Flow : 280°C, 3.00 mm 4 | 0.88 | -- | % | |
Flow : 120°C, 3.00 mm 3 | 0.040 | -- | % | |
Flow : 280°C, 3.00 mm 4 | 0.21 | -- | % | |
Water Absorption | ISO 62 | |||
Saturation, 23°C | 7.5 | -- | % | |
Equilibrium, 23°C, 50% RH | 2.2 | -- | % | |
| Hardness | Dry | Conditioned | Unit | Test Method |
Ball Indentation Hardness | 190 | 90.0 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
Tensile Modulus (23°C) | 8400 | 5100 | MPa | ISO 527-2/1 |
Tensile Stress (Break, 23°C) | 160 | 90.0 | MPa | ISO 527-2/5 |
Tensile Strain (Break, 23°C) | 3.0 | 6.0 | % | ISO 527-2/5 |
Tensile Creep Modulus | ISO 899-1 | |||
1 hr | -- | 4500 | MPa | |
1000 hr | -- | 3500 | MPa | |
Flexural Modulus 5 (23°C) | 7200 | 4200 | MPa | ISO 178/A |
Flexural Stress 5 | ISO 178/A | |||
23°C | 250 | 145 | MPa | |
3.5% Strain, 23°C | 230 | 120 | MPa | |
Flexural Strain at Flexural Strength 6 (23°C) | 5.0 | 6.0 | % | ISO 178/A |
代理德国朗盛激光焊接PA6 Durethan BKV25H2.0LT耐热老化