产品别名 |
NILAMID,玻矿增强PA66 |
面向地区 |
经销玻矿增强PA66 NILAMID A2 HH KGF2515泰科纳
| ISO | dry / cond | Unit | Test Standard |
| Density | 1470 / - | kg/m³ | ISO 1183 |
| Molding shrinkage, parallel | 0.5 | % | ISO 294-4, 2577 |
| Molding shrinkage, normal | 0.7 | % | ISO 294-4, 2577 |
| Water absorption, 23°C-sat | 5 / * | % | ISO 62 |
| Humidity absorption, 23°C/50%RH | 0.8 / * | % | ISO 62 |
| Tensile modulus | 8100 / - | MPa | ISO 527-2/1A |
| Tensile stress at break, 5mm/min | 120 / - | MPa | ISO 527-2/1A |
| Tensile strain at break, 5mm/min | 2.1 / - | % | ISO 527-2/1A |
| Charpy impact strength, 23°C | 35 / - | kJ/m² | ISO 179/1eU |
| Charpy notched impact strength, 23°C | 3 / - | kJ/m² | ISO 179/1eA |
| Izod impact notched, 23°C | 4 / - | kJ/m² | ISO 180/1A |
| DTUL at 1.8 MPa | 240 / * | °C | ISO 75-1, -2 |
| DTUL at 0.45 MPa | 252 / * | °C | ISO 75-1, -2 |
| Flammability @0.8mm nom. thickn. | HB / * | class | UL 94 |
| Flammability @3.2mm nom. thickn. | HB / * | class | UL 94 |
| Other | dry / cond | Unit | Test Standard |
| Continuous service temperature | 130 / * | °C | DIN/IEC 60216-1 |
PA66塑胶原料为半透明或不透明乳白包或带黄色颗粒状结晶形聚合物，具有可塑性。密度（g/cm3） 1．10-1．14；拉伸强度(MPa) 60. 0-80．0；洛氏硬度118；熔点252℃；脆化温度-30℃；热分解温度大于350℃；连续耐热80-120℃；冲击强度（kJ/m2） 60-100；静弯曲强度(MPa) 1 00-120；马丁耐热(℃) 50-60；弯曲弹性模量 (MPa) 2000～3000；体积电阻率（Ωcm） 1.83×1015；平衡吸水率2．5%；介电常数 1．63。
经销玻矿增强PA66 NILAMID A2 HH KGF2515泰科纳