产品别名 |
NILAMID,玻纤PTFE增强PA66 |
面向地区 |
厂家玻纤PTFE增强PA66 NILAMID A3 GF20 TF20耐磨
| ISO | dry / cond | Unit | Test Standard |
| Density | 1420 / - | kg/m³ | ISO 1183 |
| Molding shrinkage, parallel | 0.5 | % | ISO 294-4, 2577 |
| Molding shrinkage, normal | 1.0 | % | ISO 294-4, 2577 |
| Water absorption, 23°C-sat | 5.5 / * | % | ISO 62 |
| Humidity absorption, 23°C/50%RH | 0.5 / * | % | ISO 62 |
| Tensile modulus | 6300 / - | MPa | ISO 527-2/1A |
| Tensile stress at break, 5mm/min | 120 / - | MPa | ISO 527-2/1A |
| Tensile strain at break, 5mm/min | 2.5 / - | % | ISO 527-2/1A |
| Flexural modulus, 23°C | 6000 / - | MPa | ISO 178 |
| Flexural stress at max. force | 200 / - | MPa | ISO 178 |
| Charpy impact strength, 23°C | 40 / - | kJ/m² | ISO 179/1eU |
| Charpy notched impact strength, 23°C | 8 / - | kJ/m² | ISO 179/1eA |
| Izod impact notched, 23°C | 7.5 / - | kJ/m² | ISO 180/1A |
| DTUL at 1.8 MPa | 250 / * | °C | ISO 75-1, -2 |
| DTUL at 0.45 MPa | 260 / * | °C | ISO 75-1, -2 |
| Flammability @0.8mm nom. thickn. | HB / * | class | UL 94 |
| Flammability @3.2mm nom. thickn. | HB / * | class | UL 94 |
| Other | dry / cond | Unit | Test Standard |
| Continuous service temperature | 110 / * | °C | DIN/IEC 60216-1 |
PA66塑胶原料美国杜邦70G43L 高强度43%玻纤增强。
PA66美国杜邦80G33HS1-L抗冲击性 玻纤增强33% 强度 。
PA66塑胶原料美国杜邦FR10 FR15 FR50 FR60玻纤增强无卤阻燃级UL94 V-0等级
PA66美国杜邦ST801特殊级 韧性 的耐冲击性。
PA66塑胶原料日本东丽CM3001G-30一般用途 玻纤增强30%。
PA66日本东丽CM3001-N CM3006标准级尼龙-66未强化。
PA66日本东丽CM3004G-30玻纤增强30%含卤阻燃级。
PA66日本东丽CM3004-V0尼龙66未强化，无卤阻燃级。
PA66塑胶原料日本旭化成1300G高强度 高刚性 玻纤增强33%。
PA66日本旭化成1300S平衡的流动性和机械性能。
PA66日本旭化成1402S具有良好的抗热老化性能。
PA66日本旭化成FR200 FR370阻燃级UL94 V-0；不含卤素和磷。
厂家玻纤PTFE增强PA66 NILAMID A3 GF20 TF20耐磨