40GF增强PA66,安科罗PA66 |
面向地区 |
代理安科罗40%GF增强PA66 AKROMID A28GF401
Density (23°C) | 1.46 | -- | g/cm³ | ISO 1183 |
Spiral Flow 1 | 98.0 | -- | cm | Internal Method |
Molding Shrinkage | ISO 294-4 | |||
Across Flow | 0.80 | -- | % | |
Flow | 0.40 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
Tensile Modulus | 13000 | 9800 | MPa | ISO 527-2/1 |
Tensile Stress (Break) | 245 | 175 | MPa | ISO 527-2/5 |
Tensile Strain (Break) | 3.0 | 4.0 | % | ISO 527-2/5 |
| Impact | Dry | Conditioned | Unit | Test Method |
Charpy Notched Impact Strength | ISO 179/1eA | |||
-30°C | 15 | -- | kJ/m² | |
23°C | 17 | -- | kJ/m² | |
Charpy Unnotched Impact Strength | ISO 179/1eU | |||
-30°C | 80 | -- | kJ/m² | |
23°C | 95 | -- | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
Heat Deflection Temperature | ||||
0.45 MPa, Unannealed | 260 | -- | °C | ISO 75-2/B |
1.8 MPa, Unannealed | 260 | -- | °C | ISO 75-2/A |
8.0 MPa, Unannealed | 225 | -- | °C | ISO 75-2/C |
Melting Temperature 2 | 262 | -- | °C | DIN EN 11357-1 |
防静电PA，导电PA，加纤防火PA，防火PA，抗紫外线耐候PA，高温挤出级PA。
导电尼龙66：具有良好的耐磨性、耐热性、耐油性及耐化学药品性，还大大降低了原材料的吸水率和收缩率,具有优良的尺寸稳定性及的机械强度。能满足静电消散和静电放电(ESD)防护的要求。这些特殊改性材料经特殊配制，适用于从100到1012欧姆/平方(ohms/sq)的表面电阻范围，可用于注塑及挤出等成型。有很多金属和涂装的优点:零件重量较轻，较易处理，运输成本较低。它们的装配简便，制造成本较低，并且较不会受到撞凹，割损和刮伤。为了标识或美观目的，一些材料可被预先染色，避免费时且昂贵的两次着色加工。