批发安科罗增韧耐高温PA66 AKROMID A35S315
Density (23°C) | 1.11 | -- | g/cm³ | ISO 1183 |
Spiral Flow 1 | 80.0 | -- | cm | Internal Method |
Humidity Absorption - 62% RH(70°C) | 1.9 | -- | % | ISO 1110 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
Tensile Modulus | 2500 | 1200 | MPa | ISO 527-2/1 |
Tensile Stress (Yield) | 65.0 | 45.0 | MPa | ISO 527-2/50 |
Tensile Strain | ISO 527-2/50 | |||
Yield | 7.0 | 24 | % | |
Break | 30 | > 100 | % | |
Flexural Modulus 2 | 2500 | -- | MPa | ISO 178 |
Flexural Stress 2 | 95.0 | -- | MPa | ISO 178 |
Flexural Strain at Break 3 | 7.5 | -- | % | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
Charpy Notched Impact Strength | ISO 179/1eA | |||
-30°C | 13 | -- | kJ/m² | |
23°C | 15 | -- | kJ/m² | |
Charpy Unnotched Impact Strength | ISO 179/1eU | |||
-30°C | No Break | No Break | ||
23°C | No Break | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
Melting Temperature 4 | 262 | -- | °C | DIN EN 11357-1 |
| Flammability | Dry | Conditioned | Unit | Test Method |
Burning Rate 5 (1.00 mm) | <100 | -- | mm/min | FMVSS 302 |
Flame Rating (1.6 mm) | HB | -- | UL 94 |
PA66特性
1、具有优良的耐磨性、自润滑性，机械强度较高。但吸水性较大，因而尺寸稳定性较差
2、PA66在较高温度也能保持较强的强度和刚度。PA66在成型后仍然具有吸湿性，其程度主要取决于材料的组成、壁厚以及环境条件。
3、在产品设计时，一定要考虑吸湿性对几何稳定性的影响。为了提高PA66的机械特性，经常加入各种各样的改性剂。玻璃就是常见的添加剂，有时为了提高抗冲击性还加入合成橡胶，如EPDM和SBR等。PA66的粘性较低，因此流动性很好（但不如PA6）。这个性质可以用来加工很薄的元件。它的粘度对温度变化很敏感。
4、PA66的收缩率在1%~2%之间，加入玻璃纤维添加剂可以将收缩率降低到0.2%~1% 。收缩率在流程方向和与流程方向相垂直方向上的相异是较大的。PA66对许多溶剂具有抗溶性，但对酸和其它一些氯化剂的抵抗力较弱。