高刚级40玻纤PA66,巴斯夫PA66 |
面向地区 |
巴斯夫PA66 Ultramid A3WG8高刚级40%玻纤增强
Density | 1.46 | g/cm³ | ISO 1183 |
Water Absorption (Equilibrium, 23°C, 50% RH) | 1.5 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus (23°C) | 13200 | MPa | ISO 527-2 |
Tensile Stress (Break, 23°C) | 220 | MPa | ISO 527-2 |
Tensile Strain (Break, 23°C) | 3.0 | % | ISO 527-2 |
Flexural Modulus (23°C) | 12000 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength | ISO 179 | ||
-30°C | 11 | kJ/m² | |
23°C | 13 | kJ/m² | |
Charpy Unnotched Impact Strength | ISO 179 | ||
-30°C | 83 | kJ/m² | |
23°C | 95 | kJ/m² | |
Notched Izod Impact Strength | ISO 180 | ||
-40°C | 12 | kJ/m² | |
23°C | 14 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
Heat Deflection Temperature | |||
0.45 MPa, Unannealed | 260 | °C | ISO 75-2/B |
1.8 MPa, Unannealed | 250 | °C | ISO 75-2/A |
Melting Temperature (DSC) | 260 | °C | ISO 3146 |
PA66塑胶原料为半透明或不透明乳白包或带黄色颗粒状结晶形聚合物，具有可塑性。密度（g/cm3） 1．10-1．14；拉伸强度(MPa) 60. 0-80．0；洛氏硬度118；熔点252℃；脆化温度-30℃；热分解温度大于350℃；连续耐热80-120℃；冲击强度（kJ/m2） 60-100；静弯曲强度(MPa) 1 00-120；马丁耐热(℃) 50-60；弯曲弹性模量 (MPa) 2000～3000；体积电阻率（Ωcm） 1.83×1015；平衡吸水率2．5%；介电常数 1．63。
巴斯夫PA66 Ultramid A3WG8高刚级40%玻纤增强