产品别名 |
10矿物增强PBTPC,德国朗盛PBTPC |
面向地区 |
代理德国朗盛10%矿物增强PBT/PC Pocan C5211
C | Tensile modulus | 1 mm/min | MPa | ISO 527-1,-2 | 3300 |
C | Yield stress | 50 mm/min | MPa | ISO 527-1,-2 | 56 |
C | Yield strain | 50 mm/min | % | ISO 527-1,-2 | 3.4 |
C | Nominal strain at break | 50 mm/min | % | ISO 527-1,-2 | 8 |
C | Tensile Stress at break | 5 mm/min | MPa | ISO 527-1,-2 | 50 |
C | Tensile Strain at break | 5 mm/min | % | ISO 527-1,-2 | 12 |
C | Charpy impact strength | 23 °C | kJ/m² | ISO 179-1eU | 200 |
C | Charpy impact strength | -30 °C | kJ/m² | ISO 179-1eU | 150 |
C | Charpy notched impact strength | 23 °C | kJ/m² | ISO 179-1eA | 7 |
C | Charpy notched impact strength | -30 °C | kJ/m² | ISO 179-1eA | 7 |
Izod impact strength | 23 °C | kJ/m² | ISO 180-1U | 140 | |
Izod impact strength | -30 °C | kJ/m² | ISO 180-1U | 100 | |
Izod notched impact strength | 23 °C | kJ/m² | ISO 180-1A | 7 | |
Izod notched impact strength | -30 °C | kJ/m² | ISO 180-1A | 7 | |
Flexural modulus | 2 mm/min | MPa | ISO 178-A | 3550 | |
Flexural strength | 2 mm/min | MPa | ISO 178-A | 95 | |
Flexural strain at flexural strength | 2 mm/min | % | ISO 178-A | 5.2 | |
Flexural stress at 3.5 % strain | 2 mm/min | MPa | ISO 178-A | 90 | |
Thermal properties | |||||
C | Melting temperature | 10 °C/min | °C | ISO 11357-1,-3 | 225 |
C | Temperature of deflection under load | 1.80 MPa | °C | ISO 75-1,-2 | 100 |
C | Temperature of deflection under load | 0.45 MPa | °C | ISO 75-1,-2 | 120 |
Vicat softening temperature | 50 N; 120 °C/h | °C | ISO 306 | 130 | |
C | Coefficient of linear thermal expansion, parallel | 23 to 55 °C | 10-4/K | ISO 11359-1,-2 | 0.8 |
C | Coefficient of linear thermal expansion, transverse | 23 to 55 °C | 10-4/K | ISO 11359-1,-2 | 0.7 |
Other properties (23 °C) | |||||
C | Density | kg/m³ | ISO 1183 | 1290 | |
Bulk density | kg/m³ | ISO 60 | 700 |
代理德国朗盛10%矿物增强PBT/PC Pocan C5211