热稳定耐热PA66 TECHNYL A218 BLACK 21 N索尔维
Density | 1.14 | -- | g/cm³ | ISO 1183/A |
Molding Shrinkage | ISO 294-4 | |||
Across Flow | 1.5 | -- | % | |
Flow | 1.6 | -- | % | |
Water Absorption | ISO 62 | |||
24 hr, 23°C | 1.3 | -- | % | |
Equilibrium, 23°C, 50% RH | 2.9 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
Tensile Modulus (23°C) | 3300 | 1300 | MPa | ISO 527-2/1A |
Tensile Strength | ||||
Yield, 23°C | 85.0 | -- | MPa | ASTM D638 |
Yield, 23°C | 90.0 | 60.0 | MPa | ISO 527-2/1A |
Break, 23°C | 55.0 | 50.0 | MPa | ISO 527-2/1A |
Tensile Elongation | ||||
Yield, 23°C | 85 | -- | % | ASTM D638 |
Yield, 23°C | 4.0 | 10 | % | ISO 527-2 |
Break, 23°C | 30 | -- | % | ASTM D638 |
Break, 23°C | > 20 | > 300 | % | ISO 527-2 |
Flexural Modulus | ||||
23°C | 3300 | -- | MPa | ASTM D790 |
23°C | 3000 | 1300 | MPa | ISO 178 |
Flexural Strength | ||||
23°C | 125 | -- | MPa | ASTM D790 |
23°C | 120 | 70.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
Charpy Notched Impact Strength(23°C) | 4.5 | 10 | kJ/m² | ISO 179/1eA |
Charpy Unnotched Impact Strength (23°C) | No Break | No Break | ISO 179/1eU | |
Notched Izod Impact | ||||
23°C | 80 | -- | J/m | ASTM D256 |
23°C | 4.0 | 10 | kJ/m² | ISO 180 |
Unnotched Izod Impact Strength(23°C) | No Break | No Break | ISO 180/1U |
PA66美国首诺21SPC高刚性 耐化学性
PA66美国首诺R513H R533H玻纤增强，高强度，特殊热稳定，耐水解。通过FDA、UL认证。通过GM、Ford、Chryster、Delphi、Valeo
等汽车认证，适用于汽车零部件。机械部件等。
PA66德国巴斯夫A3X2G5 A3X2G7玻纤增强，红磷阻燃剂长期稳定性，具有的机械性能。
PA66塑胶原料德国巴斯夫A3EG6 A3HG5 A3EG7 A3WG6玻纤增强用于需要高刚性和尺寸稳定性的机械部件护罩。
PA66德国巴斯夫C3U高韧性 无卤素和磷阻燃级 。
PA66德国巴斯夫A3K高流动性,用于高应力工程制件如轴承，齿轮及连接器，插座。
PA66美国杜邦101F特殊级适合耐热性好的制品。
PA66塑胶原料美国杜邦101L高强度注塑级 改进机器进料和脱模特性。
PA66美国杜邦408HS注塑级良好的耐热稳定性 。
PA66美国杜邦408L特殊级 适合抗冲击性的工程制品 。
热稳定耐热PA66 TECHNYL A218 BLACK 21 N索尔维