33%玻纤增强PA66 TECHNYL A218GV33索尔维
Density | 1.39 | -- | g/cm³ | ISO 1183/A |
Water Absorption | ISO 62 | |||
24 hr, 23°C | 0.78 | -- | % | |
Saturation, 23°C | 5.3 | -- | % | |
Equilibrium, 23°C, 50% RH | 1.7 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
Tensile Modulus (23°C) | 11300 | 7800 | MPa | ISO 527-2/1A |
Tensile Strength | ||||
Break, 23°C | 190 | -- | MPa | ASTM D638 |
Break, 23°C | 195 | 140 | MPa | ISO 527-2/1A |
Tensile Elongation | ||||
Break, 23°C | 3.5 | -- | % | ASTM D638 |
Break, 23°C | 3.4 | 7.0 | % | ISO 527-2 |
Flexural Modulus | ||||
23°C | 10200 | -- | MPa | ASTM D790 |
23°C | 10000 | 7000 | MPa | ISO 178 |
Flexural Strength | ||||
23°C | 280 | -- | MPa | ASTM D790 |
23°C | 300 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
Charpy Notched Impact Strength(23°C) | 12 | 15 | kJ/m² | ISO 179/1eA |
Charpy Unnotched Impact Strength (23°C) | 90 | 100 | kJ/m² | ISO 179/1eU |
Notched Izod Impact | ||||
23°C | 120 | -- | J/m | ASTM D256 |
23°C | 12 | 18 | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
Deflection Temperature Under Load | ||||
1.8 MPa, Unannealed | 255 | -- | °C | ASTM D648 |
1.8 MPa, Unannealed | 250 | -- | °C | ISO 75-2/Af |
Melting Temperature | 262 | -- | °C | ISO 11357-3 |
PA66塑胶原料日本东丽CM3001G-30一般用途 玻纤增强30%。
PA66日本东丽CM3001-N CM3006标准级尼龙-66未强化。
PA66日本东丽CM3004G-30玻纤增强30%含卤阻燃级。
PA66日本东丽CM3004-V0尼龙66未强化，无卤阻燃级。
PA66塑胶原料日本旭化成1300G高强度 高刚性 玻纤增强33%。
PA66日本旭化成1300S平衡的流动性和机械性能。
PA66日本旭化成1402S具有良好的抗热老化性能。
PA66日本旭化成FR200 FR370阻燃级UL94 V-0；不含卤素和磷。
PA66（聚酰胺66或尼龙66），同PA6相比，PA66更广泛应用于汽车工业、仪器壳体以及其它需要有抗冲击性和高强度要求的产品。广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包内层等。
33%玻纤增强PA66 TECHNYL A218GV33索尔维
最近来访记录