批发泰科纳FRIANYL A3 GF07 V2XI阻燃7%玻纤增强PA66
| ISO | dry / cond | Unit | Test Standard |
| Density | 1420 / - | kg/m³ | ISO 1183 |
| Molding shrinkage, parallel | 0.7 | % | ISO 294-4, 2577 |
| Molding shrinkage, normal | 0.8 | % | ISO 294-4, 2577 |
| Water absorption, 23°C-sat | 6 / * | % | ISO 62 |
| Humidity absorption, 23°C/50%RH | 1.1 / * | % | ISO 62 |
| Tensile modulus | 4100 / - | MPa | ISO 527-2/1A |
| Tensile strain at yield, 50mm/min | 3.5 / - | % | ISO 527-2/1A |
| Tensile stress at break, 5mm/min | 85 / - | MPa | ISO 527-2/1A |
| Flexural modulus, 23°C | 3700 / - | MPa | ISO 178 |
| Flexural stress at max. force | 125 / - | MPa | ISO 178 |
| Charpy impact strength, 23°C | 35 / - | kJ/m² | ISO 179/1eU |
| Izod impact notched, 23°C | 4.5 / - | kJ/m² | ISO 180/1A |
| DTUL at 0.45 MPa | 250 / * | °C | ISO 75-1, -2 |
| Flammability @0.4mm nom. thickn. | V-2 / * | class | UL 94 |
| Flammability @0.8mm nom. thickn. | V-2 / * | class | UL 94 |
| Flammability @1.6mm nom. thickn. | V-2 / * | class | UL 94 |
| Flammability @3.2mm nom. thickn. | V-1 / * | class | UL 94 |
| UL recognition (0.4) | UL / * | - | UL 94 |
| Other | dry / cond | Unit | Test Standard |
| Continuous service temperature | 120 / * | °C | DIN/IEC 60216-1 |
PA66 聚酰胺66或尼龙66化学和物理特性PA66在聚酰胺材料中有较高的熔点。它是一种半晶体-晶体材料。PA66在较高温度也能保持较强的强度和刚度。在产品设计时，一定要考虑吸湿性对几何稳定性的影响。为了提高PA66的机械特性，经常加入各种各样的改性剂。玻璃就是常见的添加剂，有时为了提高抗冲击性还加入合成橡胶，如EPDM和SBR等。 PA66的粘性较低，因此流动性很好（但不如PA6）。
批发泰科纳FRIANYL A3 GF07 V2XI阻燃7%玻纤增强PA66