索尔维PA66 TECHNYL A218S40玻璃珠增强PA66
Density | 1.43 | -- | g/cm³ | ISO 1183/A |
Molding Shrinkage | ISO 294-4 | |||
Across Flow | 1.2 | -- | % | |
Flow | 1.2 | -- | % | |
Water Absorption (24 hr, 23°C) | 0.70 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
Tensile Modulus (23°C) | 5200 | 3000 | MPa | ISO 527-2/1A |
Tensile Stress (Break, 23°C) | 65.0 | 40.0 | MPa | ISO 527-2/1A |
Tensile Strain (Break, 23°C) | 5.3 | 7.5 | % | ISO 527-2 |
Flexural Modulus (23°C) | 5000 | 2600 | MPa | ISO 178 |
Flexural Stress (23°C) | 150 | 75.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
Charpy Notched Impact Strength(23°C) | 3.0 | 5.0 | kJ/m² | ISO 179/1eA |
Charpy Unnotched Impact Strength (23°C) | 25 | 130 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
Heat Deflection Temperature | ||||
0.45 MPa, Unannealed | 225 | -- | °C | ISO 75-2/Bf |
1.8 MPa, Unannealed | 95.0 | -- | °C | ISO 75-2/Af |
PA66（聚酰胺66或尼龙66），同PA6相比，PA66更广泛应用于汽车工业、仪器壳体以及其它需要有抗冲击性和高强度要求的产品。广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包内层等。