产品别名 |
30玻纤PTFE增强PA66,瑞士EMS厂家 |
面向地区 |
厂家瑞士EMS 30玻纤PTFE增强PA66 Grilon AG-30 LF15
Filler / Reinforcement |
|
Additive | LubricantPTFE + Silicone Lubricant: 15% |
Features | Low FrictionLubricatedWear Resistant |
Density | 1.46 | -- | g/cm³ | ISO 1183 |
Molding Shrinkage | ISO 294-4 | |||
Across Flow | 0.80 | -- | % | |
Flow | 0.40 | -- | % | |
Water Absorption | ISO 62 | |||
Saturation, 23°C | 5.0 | -- | % | |
Equilibrium, 23°C, 50% RH | 2.0 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
Tensile Modulus | 6500 | 3000 | MPa | ISO 527-2 |
Tensile Stress (Break) | 100 | 70.0 | MPa | ISO 527-2 |
Tensile Strain (Break) | 4.0 | 8.0 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
Charpy Notched Impact Strength | ISO 179/1eA | |||
-30°C | 3.0 | 3.0 | kJ/m² | |
23°C | 4.0 | 8.0 | kJ/m² | |
Charpy Unnotched Impact Strength | ISO 179/1eU | |||
-30°C | 30 | 30 | kJ/m² | |
23°C | 40 | 50 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
Heat Deflection Temperature | ||||
1.8 MPa, Unannealed | 190 | -- | °C | ISO 75-2/A |
8.0 MPa, Unannealed | 70.0 | -- | °C | ISO 75-2/C |
Continuous Use Temperature | ||||
-- 2 | 90.0 to 110 | -- | °C | ISO 2578 |
-- 3 | 180 | -- | °C | Internal Method |
Melting Temperature 4 | 260 | -- | °C | ISO 11357-3 |
CLTE | ISO 11359-2 | |||
Flow | 3.0E-5 | -- | cm/cm/°C | |
Transverse | 1.0E-4 | -- | cm/cm/°C |
| Flammability | Dry | Conditioned | Test Method | |
Flammability Classification (0.8 mm) | HB | -- | IEC 60695-11-10, -20 |
PA66特性
1、具有优良的耐磨性、自润滑性，机械强度较高。但吸水性较大，因而尺寸稳定性较差
2、PA66在较高温度也能保持较强的强度和刚度。PA66在成型后仍然具有吸湿性，其程度主要取决于材料的组成、壁厚以及环境条件。
3、在产品设计时，一定要考虑吸湿性对几何稳定性的影响。为了提高PA66的机械特性，经常加入各种各样的改性剂。玻璃就是常见的添加剂，有时为了提高抗冲击性还加入合成橡胶，如EPDM和SBR等。PA66的粘性较低，因此流动性很好（但不如PA6）。这个性质可以用来加工很薄的元件。它的粘度对温度变化很敏感。
4、PA66的收缩率在1%~2%之间，加入玻璃纤维添加剂可以将收缩率降低到0.2%~1% 。收缩率在流程方向和与流程方向相垂直方向上的相异是较大的。PA66对许多溶剂具有抗溶性，但对酸和其它一些氯化剂的抵抗力较弱。
厂家瑞士EMS 30玻纤PTFE增强PA66 Grilon AG-30 LF15